3D printing price-competitive with injection molding to qty 10k at @voodoomfg; game changer http://blog.voodoomfg.com/2017/08/01/summer-sale-50-off-all-direct-print-orders-with-3-day-production/ … (Via The Prepared)https://twitter.com/pencerw/status/894363505629028352 …
-
Essentially, this is so inconceivable you'd just never do it
"Cheap/few use" molds can be done in aluminum but you're still looking at qtyies significantly higher than 10 to justify mfg cost
-
-
If I understand correctly, we have to use metals because injection molding is very high pressure? What about lower-pressure mold processes?
-
Maybe the disadvantage is that no lower-pressure mold process can equal the surface finish of FDM?
-
I mean clearly vacuum forming and blow molding can be done with softer mold materials, as long as they don't melt or stick (?)
-
When I think about metal casting, the pressures are just the hydrostatic pressure of the metal; I wonder if something like that can work?
-
Casting is just not a very accurate process. Requires finishing. Follow the $
-
Do the inaccuracies in metalcasting come from sand grain, shrinkage, and solidification before filling the mold?
-
You can find books that will explain this better than I will in a tweet
-
So far I've mostly been watching YouTube videos and reading the Gingery books; are there particularly good books you can recommend?