The porosity happens during sintering, not molding. Apple doesn’t address sintering at all
-
-
Question - what’s the typical zirconia shrink rate during sintering?
Thanks. Twitter will use this to make your timeline better. UndoUndo
-
-
-
It’s simple dude, you *do not know what you’re talking about*.
Thanks. Twitter will use this to make your timeline better. UndoUndo
-
-
-
You’re a bullshit artist. And decent at it! But you know nothing about ceramic part mfg.
-
Greg, I respect you and your knowledge. Thank you for your insights.